GOLD PROCESSES

  • ALIDOR 105/145/185 - Cadmium free Pink Gold plating and/or electroforming (4N) cyanide based process producing a bright deposit for 10K, 14K and 18K
  • ALINORME 14K/18K/21K/22K® - Cadmium free Yellow Gold plating and/or electroforming Cyanide based process producing a bright deposit, up to any
    thickness, from 14K to 22K.
  • QUATUOR E – Cyanide based Gold electroforming process producing a bright deposit, up to any thickness, from 18K to 22K.
  • QUATUOR 0.7 – Cyanide based Gold electroforming process producing a bright deposit, up to any thickness, from 9K to 14K.
  • PALET AC – Acidic Gold plating process used for final Gold top plating. The colours produced are normal NIHS standards 1N14, 2N18, 3N and 3NP.
  • NICOLESS – Nickel and Cobalt free 2N acidic Gold plating process used for final Gold top plating.
  • PALET AL – Alkaline top plating process producing 1N to 5N standard Gold colours (flash).
  • GREY GOLD – Mildly acidic process producing a white-grey deposit of 22K. Contains Nickel.
  • BLACK GOLD – Mildly acidic process producing a black deposit of 14K.   Contains Nickel.
  • GREEN GOLD - Cyanide based process producing a green deposit. Contains Cadmium.
  • BROWN GOLD – Mildly acidic process producing a brown colour deposit intended for a final colour layout.
  • CORALI – Gold-Cobalt acidic process used for final colour coating, producing an intense, antique colour. It is used for decorative applications.
  • HAMILTON – Mildly acidic process producing a pale “Hamilton” colour. Used for decorative applications.
  • ACQUACLEAN 180 – Cyanide free pure gold electroforming process based on a Gold sulfite complex producing a bright yellow 24K Gold deposit.
  • HARD GOLD 24K- Pure Gold electroforming process, semi-bright, without free Cyanide. The deposit hardness is about 120-140 Hv.
  • SATINGOLD – Pure Gold electroforming process, producing a pearl-like satin deposit.
  • INOXBOND AF – Strongly acidic process especially developed for the direct treatment of Stainless Steel.
  • ACQUAPINK – Cyanide free plating process producing a bright pink Gold deposit up to 5 microns. Karatage between 16K and 18K. The deposit is composed of a Gold-Copper alloy. The shade is similar to the 4N standard colours.
  • ACQUAYELLOW – Cyanide free plating process producing a bright and levelling yellow Gold deposit up to 20 microns. Karatage between 18K and 21K.
  • ACQUAWHITE - Cyanide free plating process producing a bright and levelling white Gold deposit up to 20 microns. Karatage between 18K and 21K.
  • GOLD PEN – Alkaline Gold process producing 1N, 2N, 5N and 24K colour deposits for pen application.